Mirror Glass Safety Backing Protective Film PE Material Protection Film

Description

mirror glass safety backing protective film PE material protection film

Introduction

mirror glass safety backing protective film is one kind of strong polyethylene film coated with special acrylic pressure sensitive adhesive. It is specially designed to pass category I mirror shatter-proofing specifications on both vision and film sides. It can offer a tight bond to mirror back paints, provide an optimum performance, durability and safety to humans. when the mirrors are broken, there are no shatters all around.

Specifications

1. Description:mirror glass safety backing protective film PE material protection film

2. Material: pure PE film coated with high performance acrylic adhesive.Backing: PE Film Adhesive: high performance acrylic adhesive

3. Total thickness: 130 microns,150microns,etc,other thickness can be made as your requirement.

4.Size: 369mmx200m,629mm*200m,1219mm*200m,etc, other roll size can be made by your requirement.

5. Color: clear,white,black and white, black,etc.

6. Paper Core: 3inch

Technical data

1. Adhesion: ›5N/25mm

2. Tack:9# Steel Ball

3. Cohesion:›72hours

4. Tensile Strength: ›25MPa

5. Elongation at break: ›500%.

6. Impact Strength(A method):›250g

7. Product shelf life is 18 months from date of manufacture under normal conditions of 70℉ and 50% relative humidity.

Benefits

• Specially designed to pass category I shatter-proofing test, so that it can meet the human safety requirement.

• It is perfect for use on a safety backing or silver float glass mirrors or back painted float glass.

• High performance acrylic adhesive provides a superior adhesion to mirror backing paints.

•Meets requirements of American National standard ANSI Z97.1-1984

Application Instructions

It is suitable to all kinds of safety backing or silver float glass mirrors or back painted float glasses. The films can perform well while using the machines to apply the films; no air bubbles or winkles adhere to the paint of mirrors well.

The physical properties listed above are average values and are not to be construed as specifications. Our suggestions and recommendations for use are based on tests we believe to be reliable. However, the purchaser must determine the suitability of the product for their intended use.